OK Flux 10.72

ESAB

OK Flux 10.72

The following items have been added to your list


x

OK Flux 10.72 is an agglomerated, basic flux, designed for the production of wind towers. It combines the high demands for multi-layer thick section welding, using high deposition rates with respectable toughness values down to -50°C when combined with a standard non-alloyed SAW wire. It is used for single and multi-wire procedures such as tandem, twin arc, tandem-twin welding and many more, for butt and fillet welds. It works equally well on DC and AC current. The excellent slag removal in narrow V-joints allows the included angle of the joint to be reduced. OK Flux 10.72 can be applied for unlimited plate thicknesses. In wind tower production, plate thicknesses of 50 mm and above are common, generally welded with Y-joints. It is essential that the slag is easily removable on the first run. For the remaining filling passes the flux needs to offer a high current carrying capacity, to allow for high deposition rates, for example, 38 kg/h with the tandem twin process. Often toughness values down to -50°C are required throughout the thickness. This excellent flux can also be utilised in other market segments with similar welding requirements e.g. pressure vessels and general construction welding.


Klasifikace

Jakost S A AB 1 57 AC H5
Název EN ISO 14174

Schválení

Jakost EN 13479
Společnost CE
Schválení jsou platná podle místa výroby. Prosím kontaktujte ESAB pro další informace.

Charakteristika svařovacího materiálu

Změna legování No Silicon and moderately Manganese alloying
Index bazicity nom: 1.9
Hustota nom: 1.2 kg/dm3
Difuzní vodík max 5 ml H/100g weld metal (Redried flux)
Velikost zrna 0.315-2.0 mm (9x48 mesh)
Typ strusky Aluminate-basic

Spotřeba tavidla

V Hmotnost tavidla/1kg, drát DC Hmotnost tavidla/1kg, drát AC
26 V 0.7 kg 0.6 kg
30 V 1.0 kg 0.9 kg
34 V 1.3 kg 1.2 kg
38 V 1.6 kg 1.4 kg
A Rozměry Rychlost přesunu
580 A Ø 4.0 mm 55 cm/min

Klasifikace

Svařovací drát AWS/EN EN - po svaření Po svaření PWHT
OK Autrod 12.24 A5.23:EA2/ 14171-A:S2Mo; 24598-A:S S Mo 14171-A: S 46 3 AB S2Mo A5.23: F8A5-EA2-A3 A5.23: F8P5-EA2-A3
OK Autrod 12.22 A5.17:EM12K/ 14171-A:S2Si 14171-A: S 38 5 AB S2Si A5.17: F7A8-EM12K A5.17: F6P8-EM12K
OK Autrod 13.27 A5.23:ENi2/ 14171-A:S2Ni2 14171-A: S 46 6 AB S2Ni2 A5.23: F8A8-ENi2-Ni2 A5.23: F7P8-ENi2-Ni2
OK Autrod 12.20 A5.17:EM12/ 14171-A:S2 14171-A: S 38 5 AB S2 A5.17: F7A8-EM12 A5.17: F6P8-EM12
OK Autrod 13.64 A5.23:EA2TiB/ 14171-A:S2MoTiB A5.23: F8TA8-EA2TiB
OK Autrod 13.62 A5.23:EG/ 14171-A:SZ3TiB -

Schválení

Svařovací drát CE CWB DB DNV GL VdTÜV
OK Autrod 12.20 * - * - - *
OK Autrod 12.22 * * * * * *
OK Autrod 12.24 * - * - - *
OK Autrod 13.27 * - - - - -
*Pouze pro vybraný výrobní závod. Pro další informace prosím kontaktujte ESAB. Navštivte stránky esab.com a stáhněte si materiálový list konkrétní kombinaci tavidlo/drát kde jsou uvedeny potřebné detaily.

Typické mechanické vlastnosti

Svařovací drát Podmínky Mez skluzu Mez pevnosti v tahu Zkouška rázem Prodloužení
OK Autrod 12.20 Po svaření AWS DC+ 415 MPa
(60 ksi)
500 MPa
(73 ksi)
125 J @ -30°C,
(93 ft-lb @ -30 °F)
100 J @ -40°C,
(74 ft-lb @ -40 °F)
70 J @ -50°C,
(52 ft-lb @ -50 °F)
50 J @ -62°C,
(37 ft-lb @ -62 °F)
30 %
OK Autrod 12.22 Po svaření AWS DC+ 415 MPa
(60 ksi)
500 MPa
(73 ksi)
120 J @ -30°C,
(89 ft-lb @ -30 °F)
100 J @ -40°C,
(74 ft-lb @ -40 °F)
70 J @ -50°C,
(52 ft-lb @ -50 °F)
50 J @ -62°C,
(37 ft-lb @ -62 °F)
30 %
OK Autrod 12.24 Po svaření AWS DC+ 500 MPa
(73 ksi)
590 MPa
(86 ksi)
60 J @ -30°C,
(44 ft-lb @ -30 °F)
40 J @ -40°C,
(30 ft-lb @ -40 °F)
35 J @ -46°C,
(26 ft-lb @ -46 °F)
25 %
OK Autrod 13.27 Po svaření AWS DC+ 490 MPa
(71 ksi)
610 MPa
(88 ksi)
100 J @ -40°C,
(74 ft-lb @ -40 °F)
80 J @ -51°C,
(59 ft-lb @ -51 °F)
50 J @ -62°C,
(37 ft-lb @ -62 °F)
30 %
OK Autrod 13.62 Po svaření (acc. AWS) Plate thickness: 12mm; Heat Input: 2.2kJ/mm; Side 1: 600A, 32V, 53cm/min; Side 2: 700A, 60cm/min; DC+ 500 MPa
(73 ksi)
610 MPa
(88 ksi)
50 J @ -62°C,
(37 ft-lb @ -62 °F)
27 %
OK Autrod 13.64 Po svaření (acc. to AWS) Plate thickness 12mm Heat input 2.2kJ/mm 700A, 32V, 60cm/min DC+ 560 MPa
(81 ksi)
660 MPa
(96 ksi)
50 J @ -62°C,
(37 ft-lb @ -62 °F)
27 %

Chemické složení svarového kovu

Chemical Composition
Al2O3+MnO CaF2 CaO+MgO SiO2+TiO2
30 % 20 % 25 % 20 %
x

Kde je možné si koupit naše výrobky OK Flux 10.72

Výrobky ESAB prodáváme prostřednictvím sítě autorizovaných distributorů, kteří vám věnují pozornost a poskytují podporu a hodnotu, jakou zasluhujete. Jejich profesionalita zaručuje, že budete s nákupním procesem spokojeni stejně jako s produktem samotným.

Pro usnadnění uvádíme níže nákupní seznam online. Při procházení našich stránek můžete kliknout na libovolný produkt, a přidat jej tak do tohoto přehledného seznamu. Až budete hotovi, můžete seznam odeslat do své schránky anebo jej vytisknout a vzít jej sebou k vybranému distributorovi.

Chcete vyhledat distributora společnosti ESAB? Použijte VYHLEDAT DISTRIBUTORA, který je součástí každé stránky na našem serveru. Nebo můžete zavolat naši linku podpory a my už vás nasměrujeme tím správným směrem.


Objednací číslo a příslušenství

Objednací číslo : OK Flux 10.72
OK Flux 10.72 1000kg(2200lb) 1072H00P00
OK Flux 10.72 25kg(55lb) 1072400P0A
OK Flux 10.72 25kg(55lb) BP 1072800P00