19.12.3.L is used for welding of austenitic stainless alloys of 18% Cr - 8% Ni and 18% Cr - 10% Ni - 3% Mo-types, stabilized or non-stabilized, e.g. ASTM 316, 316L and 316Ti as well as 304, 304L, 321 and 347, used for service temperatures up to 400°C (750°F). It is also used for Cr steels with max. 19% Cr. It is used for MIG/MAG welding.

BUY NOW


Charpy V -iskusitkeys

hitsatussa tilassa

Tyypilliset lujuusarvot

MurtolujuusMyötörajaTilaVenymä
610 MPa (88 ksi)500 MPa (73 ksi)Hitsatussa tilassa39 %

Hitsausarvot

Current Voltage Langan halkaisija Wire Feed Speed
40-120 A 15-19 V 0.8 mm (0.030 in.) 4.0-8.0 m/min (157-315 in./min)
60-220 A 15-28 V 1.0 mm (0.040 in.) 4.0-12.0 m/min (157-472 in./min)
150-260 A 24-29 V 1.2 mm (0.047 in.) 3.0-10.0 m/min (118-394 in./min)
230-350 A 25-30 V 1.6 mm (1/16 in.) 3.0-5.0 m/min (118-197 in./min)

Luokittelut

Wire Electrode EN ISO 14343-A : G 19 12 3 L
SFA/AWS A5.9 : ER316L
Werkstoffnummer : 1.4430

Hyväksynnät

Laatu Luokitus EN 13479
Yhteiskunta Luokituslaitos CE
Hyväksynnät tehdaskohtaisia, lisätietoja ESABilta.

Lisäaineen ominaisuudet

Seostyyppi Austenitic (with appr. 8 % ferrite) 19 % Cr - 12 % Ni - 3 % Mo - Low C
Suojakaasu M12, M13 (EN ISO 14175)

Hitsiaineen koostumus

Langan Koostumus
C Cr Cu FN WRC-92 Mn Mo N Nb Ni P S Si
0.015 % 18.5 % 0.1 % 9 % 1.7 % 2.6 % 0.04 % 0.02 % 12 % <0.025 % 0.015 % 0.4 %
Hitsiaineen Koostumus
<0.02 % 18 % 0.1 % 7 % 1.7 % 2.5 % 0.05 % 0.01 % 12 % <0.03 % <0.02 % 0.4 %
x

Tuotenumerot ja lisätarvikkeet

Tuotenumerot : Exaton 19.12.3.L
S630089820 FIND A DISTRIBUTOR
S630084600 FIND A DISTRIBUTOR
S630099820 FIND A DISTRIBUTOR
S630109820 FIND A DISTRIBUTOR
S630129820 FIND A DISTRIBUTOR
S630169820 FIND A DISTRIBUTOR
x
x

x

Loading..