STOODY 110, 110-G, 110-O, 110-MC

Stoody

STOODY 110, 110-G, 110-O, 110-MC

The following items have been added to your list


x

Stoody 110 deposit is a modified chromium, high manganese steel used in the rebuilding of manganese steel parts subject to severe impact loading. This material offers good toughness and wear resistance, and is sometimes used as the final hardfacing layer in extreme impact situations.

BUY NOW


Features

  • Deposits cannot be flame cut but are machinable with carbide tools, are non-magnetic, and are not recommended for cast iron.
  • It can be used on carbon, low alloy, and manganese steels.
  • It also offers cavitation resistance in fluid component applications.
  • Stoody® 110 MC, G, and O are metal cored wires, producing a very light slag covering, causing no interference in multi-layer welding.


Typical Tensile Properties

As Deposited Work Hardened
17 HRC 55 HRC
Tensile Strength 119 MPa (820 ksi)
Yield Strength 76 MPa (524 ksi)
Elongation 40 %

Deposition Data

Current Deposition Type Diameter TTW Dist. Voltage
150-210 A Full Range 1.6 mm (1/16 in.) 13-25 mm (1/2-1 in.) 22-26 V
225-275 A Full Range 2.0 mm (5/64 in.) 19-32 mm (3/4-1 1/4 in.) 24-26 V
225-300 A Full Range 2.4 mm (3/32 in.) 25-38 mm (1-1 1/2 in.) 23-27 V
225-375 A Full Range 2.8 mm (7/64 in.) 25-38 mm (1-1 1/2 in.) 23-27 V

Typical Weld Metal Analysis %

C Cr Fe Mn Other
0.5 % 17.0 % BAL % 15.0 % 1.0 %